Analysis on Hot Pressing Forming Technology of SAE4130 Steel Tube
Han Dong， Zou Feng， Yuan Jiao
Abstract:SAE4130 belongs to medium carbon tempered alloy steel with high carbon content.Taking SAE4130 steel tube as the research object，plastic forming tests are carried out under different temperature conditions，and the law of SAE4130 steel tube plastic forming under different temperature conditions is studied by means of microstructure observation，tensile test and hardness test.The results show that SAE4130 steel has better plasticity and can achieve greater degree of plastic deformation under heating.With the increase of heating temperature，martensite content is decreased，while bainite content is increased.At this time，the pipe end is plastic formed，and the quality of the forming part is the best.
Keywords:SAE4130 steel pipe；plastic forming；hot forming